自包裹型铜/因瓦类合金复合材料的设计、制备技术及其热物理性能研究

This project, based on the main academic thinking of the integration of design and experiment, studies the compositional design, morphology control, preparation techniques and thermo-physical properties of its sintered alloys of self-organized Cu/Invar alloy composite powders. Based on the experimental data of the phase equilibria in this study and the related information of phase diagrams in the literatures, the thermodynamic database of Cu-Fe-Co-Ni-Cr-Nb-Mo multi-component system will be established. By considering the requirement for the composition of Invar alloy, self-organized Cu/Invar alloy composite powders will be designed based on the composition and temperature ranges of stable miscibility gap of liquid phase obtained from the calculated phase diagrams. Afterwards, self-organized Cu/Invar alloy composite powders will be prepared by the gas atomization. With investigating the effect of the processing parameters such as the alloy composition, liquid volume fraction, melting temperature and solidification rate on the morphology of solidification，the optimum preparative process will be determined. By combining with hot pressing sintering technology, we will investigate the properties of thermal expansion and thermal conductivity of the sintered composite materials made of self-organized Cu/Invar alloy composite powders in different alloy systems，and explore the best preparative process conditions of the Cu/Invar alloy composite materials with the properties of low expansion and high thermal conductivity. This study will provide technical reserves for the development of such composites in some alloy systems with liquid phase separation.

本项目以设计和制备一体化为主要学术思想，研究自包裹型铜/因瓦类合金复合粉体材料的成分设计、组织控制、制备技术及其烧结体材料的热物理性能。基于本研究中实验测定的相平衡结果与文献报道的相图信息，建立Cu-Fe-Co-Ni-Cr-Nb-Mo多元合金的热力学数据库。通过计算相图有效地预测稳定液相分离存在的成分和温度范围，并考虑因瓦合金对成分的要求，设计自包裹型铜/因瓦类合金复合粉体的合金成分。在此基础上，利用雾化制粉技术，制备铜/因瓦类合金复合粉体材料，并考察合金成分、液相的体积分数、熔炼温度、凝固速度等工艺参数对凝固组织形态的影响，确定制备该类复合粉体材料的最佳工艺。并结合热压烧结技术，研究不同体系的自包裹型铜/因瓦类合金复合粉烧结体材料的热膨胀性能和导热性能，探索利用液相分离制备低膨胀高导热铜/因瓦类合金复合材料的工艺条件，为该类复合材料的研发提供技术积累。

本项目以设计和制备一体化为主要学术思想，研究自包裹型铜/因瓦类合金复合粉体材料的成分设计、组织控制、制备技术及其烧结体材料的热物理性能。本项目实验测定了Cu-Co-Mo、Fe-Mo-Nb等13个三元系在不同温度时的相平衡，完善了Cu基多元合金系的实验相图信息。在此基础上，利用CALPHAD方法，对Cu-Co-Mo、Fe-Mo-Nb等多个体系相图进行了热力学优化与计算，充分考虑了所有基础二元系和三元系热力学模型的统一性和参数的兼容性，建立了液相分离型Cu-Fe-Co-Cr-Ni-Mo-Nb多元合金热力学数据库。通过计算相图有效地预测了稳定液相分离存在的成分和温度范围，成功实现了一系列自包裹型Cu/(Fe0.37Co0.54Cr0.09)100-x(W/Nb/Ag)x复合粉体的成分与组织设计。并利用雾化制粉技术，制备了自包裹型铜/因瓦类合金复合粉体。并考察合金成分、液相的体积分数、熔炼温度、凝固速度等工艺参数对凝固组织形态的影响，确定了制备该类复合粉体材料的最佳工艺。并结合热压烧结技术，在900-950 ºС、压力为50 MPa，烧结2h后获得了致密度在98 %以上的烧结体材料，最终获得具有热膨胀系数范围为5.75~10.66×10-6 ºС-1，热导率范围为42.2~107.4 W·m-1·K-1的Cu/Fe37Co54Cr9基合金复合粉烧结体材料。此外，Ag微合金化的Cu45(Fe0.37Co0.54Cr0.09)47Ag8复合粉烧结体材料的综合热物理性能相比于Cu45(Fe0.37Co0.54Cr0.09)55烧结体材料的热物理性能 (热膨胀系数11.39×10-6 K-1和热导率61.4 W·m-1·K-1)有了明显的提升。本项目中所制备的Cu/Fe37Co54Cr9基合金复合粉体均具有自包裹型复合结构，部分烧结体材料可以满足电子封装材料的高导热和低膨胀特性。